LFT PA66+30GF (Long Fiber Reinforced Nylon 66 with 30% Glass Fiber) provides optimized mechanical strength, superior impact resistance, and enhanced thermal stability. Designed for automotive, industrial, and structural applications, it ensures high durability, lightweight efficiency, and high adaptability.
Product Overview
LFT PA66+30GF is a high-performance long fiber reinforced Nylon 66 material, offering a unique combination of high rigidity, high toughness, and excellent self-lubricating properties. This material is particularly suitable for components that need to withstand high mechanical loads and friction forces. With superior wear resistance and thermal stability, it ensures long-term performance even in demanding working environments.
Key Features
- High Rigidity & High Toughness: The glass fiber reinforcement provides outstanding rigidity and toughness, making the material ideal for high-load and impact-resistant applications.
- Excellent Self-Lubrication: The material’s surface offers natural self-lubricating properties, reducing friction and wear, thus extending the life of the components.
- Wear & Heat Resistance: It excels in high-temperature and high-friction environments, ensuring stability and durability even under extreme conditions.
Applications
- Handbrake Components: Suitable for various parts of handbrake systems, the material maintains long-term stable performance under frequent use and enhances the overall service life of the components.
| Test Properties | Unit | Test Method | Test Condition | Typical Value |
| Physical Properties | ||||
| Density | g/cm³ | ISO 1183 | 1.38 | |
| Filler Content | % | ISO 1172 | 30 | |
| Mold Shrinkage | % | ISO 294 | Parallel: 0.20, Vertical: 0.60 | |
| Mechanical Properties | ||||
| Tensile Strength | MPa | ISO 527 | Type I sample, 50mm/min | 195 |
| Elongation at Break | % | ISO 527 | Type I sample, 50mm/min | - |
| Flexural Strength | MPa | ISO 178 | 23℃, 10mm/min | 252 |
| Flexural Modulus | MPa | ISO 178 | 23℃, 10mm/min | 8100 |
| Izod Impact Strength (Notched) | KJ/m² | ISO 180 | 23℃ | 28 |
| Charpy Impact Strength (Unnotched) | KJ/m² | ISO 179 | 23℃ | 76 |
| Thermal Properties | ||||
| Melting Point | ℃ | ISO 3146 | 246 | |
| Heat Deflection Temperature (HDT) | ℃ | ISO 75-2-2004 | 1.8MPa | - |
| Flammability | ||||
| Flammability of Automotive Interior Parts | ≤100 |