new material
LFT PA6+50GF (Long Fiber Reinforced Nylon 6 with 50% Glass Fiber) provides optimized mechanical strength, superior impact resistance, and enhanced thermal stability. Designed for automotive, industrial, and structural applications, it ensures long-term durability, lightweight efficiency, and high adaptability.
Product Overview
LFT PA6+50GF is a long fiber reinforced Nylon 6 material, offering superior rigidity and weather resistance. It is particularly suited for industrial applications that require high strength, impact resistance, and aging resistance. This material is ideal for use in extreme environments, providing high compressive and tensile strength, and is widely used for components that need to bear substantial mechanical loads.
Key Features
- High Rigidity: With 50% glass fiber content, this material exhibits exceptional rigidity under mechanical load, ensuring excellent structural stability.
- Weather Resistance: Outstanding UV and weather resistance, making it ideal for components exposed to outdoor conditions for prolonged periods.
- High Strength and Durability: The long fiber reinforcement significantly enhances the material's tensile strength and impact resistance, ensuring high durability and longevity in demanding environments.
Applications
- Safety Shoe Toe Support: The material is ideal for the toe support of safety shoes, providing additional strength and durability to the toe area, enhancing protection for the wearer.
| Test Properties | Unit | Test Method | Test Condition | Typical Value |
| Physical Properties | ||||
| Density | g/cm³ | ISO 1183 | 1.57 | |
| Filler Content | % | ISO 1172 | 50 | |
| Mold Shrinkage | % | ISO 294 | Parallel: 0.15, Vertical: 0.50 | |
| Mechanical Properties | ||||
| Tensile Strength | MPa | ISO 527 | Type I sample, 50mm/min | 220 |
| Elongation at Break | % | ISO 527 | Type I sample, 50mm/min | - |
| Flexural Strength | MPa | ISO 178 | 23℃, 10mm/min | 310 |
| Flexural Modulus | MPa | ISO 178 | 23℃, 10mm/min | 12900 |
| Izod Impact Strength (Notched) | KJ/m² | ISO 180 | 23℃ | 42 |
| Charpy Impact Strength (Unnotched) | KJ/m² | ISO 179 | 23℃ | 86 |
| Thermal Properties | ||||
| Melting Point | ℃ | ISO 3146 | 215 | |
| Heat Deflection Temperature (HDT) | ℃ | ISO 75-2-2004 | 1.8MPa | - |
| Flammability | ||||
| Flammability of Automotive Interior Parts | ≤100 |