new material
PA6 + 25% GF (25% Glass Fiber Reinforced Nylon 6) provides optimized mechanical strength, superior impact resistance, and enhanced dimensional stability. Designed for automotive components, industrial applications, and structural parts, it ensures long-term durability, lightweight efficiency, and high adaptability.
Product Overview
PA6 + 25% GF is a reinforced Nylon 6 material, incorporating 25% glass fiber, providing excellent mechanical strength and electrical performance. This material is capable of withstanding high loads and harsh environments, making it ideal for use in mechanical and automotive components. It excels in applications requiring high wear resistance and strength.
Key Features
- High Mechanical Strength: The 25% glass fiber reinforcement gives the material extremely high tensile strength and rigidity, making it suitable for high-load applications.
- Excellent Electrical Properties: The material provides outstanding electrical insulation, making it ideal for various electrical and electronic components.
- Superior Wear Resistance: Reinforced material demonstrates excellent wear resistance, suitable for high-friction environments.
Applications
PA6 + 25% GF is widely used in applications requiring high strength, wear resistance, and stability, including:
- Mechanical Components: Suitable for high-strength mechanical parts such as gears, bearings, frames, and other load-bearing components.
- Automotive Components: Ideal for critical automotive parts such as engine components, housings, connectors, and other high-stress applications.
| Test Item | Unit | Test Method | Test Condition | Typical Values |
| Physical Property | ||||
| Density | g/cm³ | ISO 1183 | - | 1.32 |
| Filler Content | % | ISO 1172 | GF25 | - |
| Mold Shrinkage | % | ISO 294 | Parallel 0.3, Vertical 0.7 | - |
| Mechanical Property | ||||
| Tensile Strength | MPa | ISO 527 | I-type sample, 50mm/min | 155 |
| Elongation at Break | % | ISO 527 | I-type sample, 50mm/min, Gauge 50mm | 3 |
| Flexural Strength | MPa | ISO 178 | 23℃, 10mm/min | 205 |
| Flexural Modulus | MPa | ISO 178 | 23℃, 10mm/min | 6800 |
| Izod Impact Strength (Notched) | KJ/m² | ISO 180 | 23℃ | 11 |
| Charpy Impact Strength (Unnotched) | KJ/m² | ISO 179 | 23℃ | 70 |
| Thermal Property | ||||
| Melting Point | ℃ | ISO 11357-1 | - | 220 |
| Heat Deflection Temperature | ℃ | ISO 75 | 0.45MPA 219℃, 1.8MPA 205℃ | 219, 205 |
| Flammability | ||||
| Flammability Class | UL-94 | - | HB | |
| Glow Wire Ignition Temperature | ℃ | IEC 60695-2-13 | - | - |
| Electrical Property | ||||
| Surface Resistivity | Ω | IEC 60093 | - | 100000000000000 |
| Volume Resistivity | Ω•cm | IEC 60093 | - | 1000000000000000 |