Heat-Resistant Reinforced Polylactic Acid (PLA) Resin is a biodegradable thermoplastic with superior thermal stability and mechanical strength. Ideal for high-temperature applications, it ensures durability, environmental sustainability, and enhanced performance in industrial and packaging solutions.
Product Overview
IM9004B is a heat-resistant reinforced polylactic acid resin, designed through the modification of polylactic acid technology. This high-performance material combines the biodegradability of polylactic acid with enhanced heat resistance, making it suitable for the production of plastic products used in high-temperature environments. It also complies with food contact safety standards.
Product Features
- Enhanced Heat Resistance:Modified polylactic acid improves the material's heat resistance, making it suitable for long-term use in high-temperature environments.
- Biodegradability:Completely biodegradable, environmentally friendly and non-toxic.
- Food Contact Safety:Meets food contact standards, safe and reliable for use with food.
- Strong Processability:Easy to inject and mold, suitable for various plastic forming processes.
Applications
- Non-Disposable Heat-Resistant Tableware:Such as plates, bowls, cups, spoons, chopsticks, and more.
- Daily Use Plastic Products:Including combs, toothbrushes, stationery, and more.
| Test Item | Typical Value | Testing Standard |
| Density | 1.28 g/cm³ | ISO 1183 |
| Melt Index | 210℃, 2.16kg | 10-20 g/10min |
| Mold Shrinkage | 0.1-0.3% | ISO 294 |
| Tensile Strength | 10mm/min | 65 MPa |
| Elongation | 10mm/min | 6% |
| Flexural Strength | 2mm/min | 100 MPa |
| Flexural Modulus | 2mm/min | 4500 MPa |
| Notched Impact Strength | 4mm, 23℃ | 3 kJ/m² |
| Melting Point | 10℃/min | 160-170℃ |
| Heat Deflection Temperature HDT/B | 0.45MPa | 110℃ |