LFT PA6+40GF (Long Fiber Reinforced Nylon 6 with 40% Glass Fiber) provides optimized mechanical strength, superior impact resistance, and enhanced thermal stability. Designed for automotive components, industrial applications, and structural parts, it ensures long-term durability, lightweight efficiency, and high adaptability.
Product Overview
LFT PA6+40GF is a long fiber reinforced Nylon 6 material, offering outstanding high rigidity, weather resistance, and excellent physical properties. This material is especially suitable for components requiring high strength and durability. It is widely used in industrial and construction applications, particularly in environments where high-temperature and UV resistance are critical.
Key Features
- High Rigidity: Enhanced with long glass fibers, the material offers exceptional rigidity, ensuring structural stability under high load conditions.
- Weather Resistance: Excellent UV stability and aging resistance, making it ideal for outdoor applications in various climate environments.
- High Strength: Exceptional tensile strength and impact resistance, allowing the material to perform reliably in harsh environments over long periods.
Applications
- Manhole Cover Tops: Ideal for manhole cover tops, providing the necessary strength and durability for long-term use in various environments.
- Buoy Joint Components: Used in buoy joint components and other marine applications, ensuring stability and corrosion resistance for prolonged use in water.
| Test Properties | Unit | Test Method | Test Condition | Typical Value |
| Physical Properties | ||||
| Density | g/cm³ | ISO 1183 | 1.43 | |
| Filler Content | % | ISO 1172 | 40 | |
| Mold Shrinkage | % | ISO 294 | Parallel: 0.20, Vertical: 0.60 | |
| Mechanical Properties | ||||
| Tensile Strength | MPa | ISO 527 | Type I sample, 50mm/min | 185 |
| Elongation at Break | % | ISO 527 | Type I sample, 50mm/min | - |
| Flexural Strength | MPa | ISO 178 | 23℃, 10mm/min | 286 |
| Flexural Modulus | MPa | ISO 178 | 23℃, 10mm/min | 11200 |
| Izod Impact Strength (Notched) | KJ/m² | ISO 180 | 23℃ | 38 |
| Charpy Impact Strength (Unnotched) | KJ/m² | ISO 179 | 23℃ | 89 |
| Thermal Properties | ||||
| Melting Point | ℃ | ISO 3146 | 215 | |
| Heat Deflection Temperature (HDT) | ℃ | ISO 75-2-2004 | 1.8MPa | - |
| Flammability | ||||
| Flammability of Automotive Interior Parts | ≤100 |